| FEROCAST 102 |
Size (mm) : 3.15 4.00
Current (amps) : 80-120 100-150
|
For conditioning the contaminated surface on cast iron prior to use of
superior machinable cast iron product. Deposits are quick
freezing type and non-machinable.
|
|
| CACI 150 |
HARDNESS : 140 - 180 BHN
2 U.T.S. : 37 - 44 kgf/mm
Size (mm) : 2.50 3.15 4.00 5.00
Current (amps) : 40-70 70-110 90-120 120-170
|
CAC1150 is an electrode with Ferro Nickel core wire for welding cast iron
without preheating. Recommended for repairing of cast iron, filling foundry
defects with perfect colour match. Can be used for malleable and S.G. Iron.
|
|
| CINOD 160 |
TENSILE STRENGTH : 35 - 40 kgf/mm2
HARDNESS : 150-210 BHN
Size (mm) : 2.50 3.15 4.00 5.00
Current (amps) : 50-85 80-120 100-140 120-170
|
A high nickel type of electrode formulated for high strength joining of
nodular iron with exceptional crack resistivity. The deposits are machinable.
Suitable for pump casing, valve bodies, valve flanges, beli housing, motor covers etc.
|
|
| CACI 540 |
TENSILE STRENGTH : 35 - 40 kgf/mm2
HARDNESS : 140 -170 BHN
Size (mm) : 3.15 4.00 5.00
Current (amps) : 45-75 75-110 100-140 130-170
|
A newly formulated lo-heat input, highly crack resistant cast iron electrode
for Nodular iron casting, malleable, as well as grey irons with excellent machinability.
Recommended for high strength joints on C.l. housings, dies & for joining cst irons to steels.
|
|
| CACI 650 |
TENSILE STRENGTH : 30 - 35 kgf/mm2
Size (mm) : 2.50 3.15 4.00 5.00
Current (amps) : 45-75 75-110 100-140 130-170
|
A new economical nickel alloy for build up and joining various types of cast
iron and cast iron to steels. The deposits are machinable and very much
suitable for filling up cast iron castings, pump bodies, rebuilding missing sections etc.
|
|
| GRELOY 850 |
TENSILE STRENGTH : 30 - 35 kgf/mm2
HARDNESS : 150 -180 BHN
Size (mm) : 2.50 3.15 4.00 5.00
Current (amps) : 45-90 60-110 80-130 100-170
|
A pure nickel electrode for maximum machinability, suitable for build up as
well as for joining various types of cast iron and cast iron to steels. Applications include machine bases, cylinder blocks,
motor / generator/pump casings, impeller, machine slide etc.
|
|
| SUPERCINOD 1600 |
TENSILE STRENGTH : 40 - 48 kgf/mm2
2 YIELD STRENGTH : 30 - 40 kgf/mm
HARDNESS : 150 - 200 BHN
Size (mm) : 2.50 3.15 4.00 5.00
Current (amps) : 50-85 80-120 100-140 100-170
|
A special cast iron electrode with high recovery. Specially designed for
ductile, machinable and crack resistant repair welding on grey, nodular
cast iron and malleable iron and joining same to steel. Recommended
for use on dirty, aged & burnt cast iron.
|
|
| NODURON 60 |
TENSILE STRENGTH : 45 - 50 kgf/mm2
HARDNESS : 180 BHN
Elongation (l=5d) : 15% (Min.)
CVN Impact (–20° C) : 75 J (Min.)
Size (mm) : 3.15 4.00 5.00
Current (amps) : 70-100 120-160 160-210
|
A specially developed basic graphite coated electrode consisting of a very
complex flux chemistry. The flux coating is designed to give a fully covering slag,
which can be easily removed after the bead is cooled. Hence both the transition zone as well as HAZ are FULLY MACHINABLE,
even with a HIGH SPEED STEEL TOOL. It used for welding all types of cast irons - Grey
cast iron, malleable cast iron, nodular cast iron or ductile iron-pearlitic
as well as ferritic varieties. It can also weld cast iron to steel, dirty,
oily cast irons thick to thin cast irons.
|
|